MATERIAIS CERÂMICOS SUPERCONDUTORES APRESENTAM PROPRIEDADES IMPORTANTES PARA APLICAÇÕES TECNOLÓGICAS. A PRINCIPAL PROPRIEDADE, RESPOSTA MAGNÉTICA DEPENDE FORTEMENTE DA ROTA DE SÍNTESE, MÉTODO DE PROCESSAMENTO, E PRINCIPALMENTE DA ESTEQUIOMETRIA DO MATERIAL. NO PRESENTE TRABALHO, FORAM ESTUDADAS ALGUMAS VARIAÇÕES ENVOLVIDAS NAS CONDIÇÕES DE SÍNTESE DE PÓS CERÂMICOS DO COMPOSTO YBA2CU3O7-D SINTETIZADOS ATRAVÉS DO MÉTODO PECHINI. COM A FINALIDADE DE VERIFICAR-SE AMOSTRAS COM O MENOR TEOR DA FASE SECUNDÁRIA CARBONATO DE BÁRIO (BACO3), UTILIZOU-SE AS VARIAÇÕES DE PH EM 3, 7 E 10 EM AMOSTRAS COM E SEM A UTILIZAÇÃO DO ÁCIDO ETILENODIAMINOTETRACÉTICO (EDTA) NA SÍNTESE DO PRECURSOR POLIMÉRICO. BUSCOU-SE TAMBÉM MELHOR COMPREENDER OS PROCESSOS FÍSICO-QUÍMICOS PRESENTES NAS DIFERENTES ETAPAS DA PREPARAÇÃO DAS AMOSTRAS. AINDA NESSE ESTUDO, FEZ-SE TRATAMENTOS TÉRMICOS EM 400 OC, 700 OC E 900 OC PARA UMA AVALIAÇÃO QUALITATIVA DAS PARTÍCULAS. FOI UTILIZADO COMO FONTE DE CÁTIONS, ÓXIDOS DE ÍTRIO E COBRE, ALÉM DE CARBONATO DE BÁRIO. COMO AGENTE COMPLEXANTE O ÁCIDO CÍTRICO (AC) E COMO AGENTE POLIMERIZANTE O ETILENOGLICOL (EG). A RESINA POLIMÉRICA FOI CARACTERIZADA USANDO-SE ANÁLISE TÉRMICA DIFERENCIAL (DTG), TERMOGRAVIMETRIA (TG) COM ACOPLAMENTO À ESPECTROFOTOMETRIA NO INFRAVERMELHO (IRFT) E CALORIMETRIA EXPLORATÓRIA DIFERENCIAL (DSC). TAIS CARACTERIZAÇÕES FORAM FEITAS DE FORMA A RELACIONAR A ESTRUTURA, CONDIÇÕES DE SÍNTESE E FENÔMENOS QUE OCORREM EM CADA INTERVALO DE TEMPERATURA. O PRODUTO DA PIRÓLISE DA RESINA, DENOMINADO DE ?PUFF?, FOI DESAGLOMERADO E CALCINADO A DIFERENTES TEMPERATURAS, SOB ATMOSFERA AMBIENTE, PERMITINDO-SE O ACOMPANHAMENTO DA EVOLUÇÃO DAS FASES CRISTALOGRÁFICAS POR DIFRAÇÃO DE RAIO-X (DRX), SENDO A MORFOLOGIA DOS PÓS, VERIFICADA POR MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV). POR MEIO DOS DADOS OBTIDOS, PERCEBE-SE QUE AS AMOSTRAS PREPARADAS EM PH PRÓXIMO DE 7, SEM A ADIÇÃO DE EDTA E CALCINADAS EM TEMPERATURAS DE 900 OC FORAM AS QUE APRESENTARAM MENOR FORMAÇÃO DE FASE SECUNDÁRIA.

Palavras-Chave (EN):

Resumo Original (EN):

CERAMIC SUPERCONDUCTING MATERIALS PRESENT SIGNIFICANT PROPERTIES FOR TECHNOLOGICAL APPLICATIONS. THESE PROPERTIES STRONGLY DEPEND ON THE SYNTHESIS ROUTES, PROCESSING METHODS, AND MAINLY ON THE CHEMICAL STOICHIOMETRY OF THE PREPARED COMPOUNDS. IN THIS WORK SOME STEPS AND VARIATIONS ON THE SYNTHESIS CONDITIONS OF YBA2CU3O7-D (YBCO) WERE STUDIED BY USING THE SOL-GEL TECHNIQUE, KNOWN AS THE PECHINI METHOD. THE INFLUENCE OF PH AND THE USE OF ETILENODIAMINOTETRACETIC ACID (EDTA) IN THE SYNTHESIS OF THE YBCO PHASE, AS WELL AS A POSSIBLE FORMATION OF BACO3 AS A SECONDARY UNDESIRABLE PHASE WERE TESTED. OXIDES AND CARBONATES WERE USED AS METALLIC SALTS, ACID CITRIC (CA) AND THE ETHYLENE-GLYCOL (EG) WERE USED AS COMPLEXING AGENT AND POLYMERIZATION AGENT, RESPECTIVELY. THE POLYMERIC RESIN WAS CHARACTERIZED BY DIFFERENTIAL THERMAL ANALYSIS (DTA/DSC) AND THERMOGRAVIMETRIC ANALYSIS (TG) ASSOCIATED WITH INFRARED SPECTROSCOPY (IRFT), TRYING TO RELATE THE POLYMER STRUCTURE AND THE SYNTHESIS CONDITIONS FOR EACH TEMPERATURE. AFTER THAT, THE POLYMERIC GEL WAS PYROLEZED IN A TEMPERATURE OF 200OC, GROUND AND HEAT-TREATED UNDER DIFFERENT TEMPERATURES, ALLOWING THE STUDY OF THE CRYSTALLOGRAPHIC PHASE EVOLUTION BY USING X-RAY DIFFRACTION (XRD). THE POWDER MORPHOLOGY WAS ALSO ANALYZED BY MEANS OF SCANNING ELECTRON MICROSCOPY (SEM). THE OBTAINED RESULTS INDICATED THAT THE SAMPLES PREPARED USING PH CLOSE TO 7, WITHOUT THE USE OF EDTA UNDER A TEMPERATURE OF 900 OC, PRESENTED SMALLER AMOUNT OF SECONDARY PHASES.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por