TITANATOS DE BÁRIO (BT) E DE ESTRÔNCIO (ST) FORAM PRODUZIDOS UTILIZANDO DOIS MÉTODOS DIFERENTES, REAÇÃO DO ESTADO SÓLIDO (SSR), NAS TEMPERATURAS DE 1150 E 1200°C, E HIDROTÉRMICO ASSISTIDA POR MICRO-ONDAS (MAH), COM CONCENTRAÇÕES DIFERENTES DO MINERALIZADOR KOH (1, 3 E 6 MOL/L). CLORETO DE BÁRIO/ESTRÔNCIO E TIO2 NA FASE ANATASE FORAM UTILIZADOS COMO PRECURSORES NO PREPARO PELO MÉTODO SSR. PARA AS SÍNTESES REALIZADAS COM AUXÍLIO DO MÉTODO MAH, FORAM UTILIZADOS OS MESMOS CLORETOS E, COMO PRECURSOR DE TITÂNIO, UM COMPLEXO DE ANATASE COM PERÓXIDO DE HIDROGÊNIO (30 VOLUMES). EM TODAS AS ELABORAÇÕES, OS TITANATOS FORAM OBTIDOS, PORÉM, COM RESULTADOS DIFERENTES NA CRISTALIZAÇÃO E MORFOLOGIA DAS PARTÍCULAS, QUE PODEM SER ASSOCIADOS ÀS DIFERENTES CONCENTRAÇÕES DO MINERALIZADOR, AO TIPO DE PRECURSOR DE TITÂNIO UTILIZADO, BEM COMO PELO EMPREGO DE DIFERENTES ESTRATÉGIAS DE SÍNTESE. OS MATERIAIS RESULTANTES DOS DOIS PROCESSOS FORAM CARACTERIZADOS POR DIFERENTES TÉCNICAS, TAIS COMO, DIFRATOMETRIA DE RAIOS-X (DRX), ESPECTROSCOPIA MICRO-RAMAN (MR), ESPECTROSCOPIA NA REGIÃO DO INFRAVERMELHO COM TRANSFORMADA DE FOURIER (FTIR), UV-VIS, MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) E, FINALMENTE, SUAS EMISSÕES FOTOLUMINESCENTES (FL) FORAM REGISTRADAS A TEMPERATURA AMBIENTE. COMO ESPERADO, OCORRERAM DIFERENÇAS NA CRISTALINIDADE, MORFOLOGIA, QUANTIDADE DE FASES E FOTOLUMINESCÊNCIAS ENTRE OS TITANATOS PRODUZIDOS PELAS DUAS TÉCNICAS. NO MÉTODO MAH, AS CONCENTRAÇÕES DAS FASES BT E ST AUMENTAM COM O AUMENTO DA CONCENTRAÇÃO DE KOH E A FASE BT, COM 6 MOL/L DESSE MINERALIZADOR, É OBTIDA COM MORFOLOGIA DEFINIDA E COM MAIOR PUREZA DO QUE NA FASE ST. O KOH AUXILIA NA CO-PRECIPITAÇÃO DE HIDRÓXIDOS DURANTE A SÍNTESE, SENDO QUE ESTE MINERALIZADOR APRESENTA UMA FORTE INFLUÊNCIA SOBRE O CÁTION QUE OCUPARÁ O SÍTIO A. NO MÉTODO SSR, A FASE ST É OBTIDA A PARTIR DE 1150°C, ENQUANTO QUE A FASE BT SÓ É FORMADA EM 1200°C. FORAM OBSERVADAS MUDANÇAS RELATIVAS NAS ENERGIAS DO BAND GAP E NA EMISSÃO FOTOLUMINESCENTE DAS AMOSTRAS, PARA CADA MÉTODO DE SÍNTESE. OS RESULTADOS MOSTRAM QUE A FASE ANATASE, COMO PRECURSOR DE TITÂNIO, É EFETIVO NO PROCESSO DE SÍNTESE DOS TITANATOS UTILIZANDO O MÉTODO MAH. ESTES MATERIAIS APRESENTAM PROPRIEDADES QUE INDICAM POSSIBILIDADES DE APLICAÇÕES EM DISPOSITIVOS ÓPTICOS.

Palavras-Chave (EN):

Resumo Original (EN):

BARIUM TITANATE (BT) AND STRONTIUM TITANATE (ST) WERE PRODUCED BY TWO DIFFERENT METHODS: SOLID STATE REACTION (SSR), AT 1150 AND 1200ºC; AND MICROWAVE ASSISTED HYDROTHERMAL (MAH), WITH THREE CONCENTRATIONS OF THE MINERALIZER KOH (1, 3 AND 6 MOL/L). BARIUM/STRONTIUM CHLORIDES AND TIO2 (ANATASE PHASE) WERE USED AS PRECURSORS IN THE PREPARATION BY THE SSR METHOD. FOR THE SYNTHESIS PERFORMED BY THE MAH METHOD, WERE USED THE SAME CHLORIDES AND, AS TITANIUM PRECURSOR, AN ANATASE COMPLEX WITH HYDROGEN PEROXIDE (30 VOLUMES) WAS USED. IN ALL SYNTHESIS, TITANATES WERE OBTAINED SUCEFULLY, HOWEVER, DIFFERENT RESULTS IN CRYSTALIZATION AND MORPHOLOGY WAS OBSERVED. THIS MAY BE ASSOCIATED TO DIFFERENT CONCENTRATIONS OF THE MINERALIZER, THE TYPE OF TITANIUM PRECURSOR USED AND THE USE OF DIFFERENT SYNTHESIS STRATEGIES. THE RESULTING MATERIALS OF THE TWO METHODS WERE CHARACTERIZED BY DIFFERENT TECHNIQUES, SUCH AS X-RAY DIFFRACTION (XRD), MICRO-RAMAN SPECTROSCOPY (MR), FOURIER TRANSFORM INFRARED SPECTROSCOPY (FTIR), UV-VIS, SCANNING ELECTRON MICROSCOPY (SEM) AND FINALLY THEIR PHOTOLUMINESCENT EMISSIONS (PL) WERE RECORDED AT ROOM TEMPERATURE. AS EXPECTED, THERE WERE DIFFERENCES IN CRYSTALLINITY, MORPHOLOGY, NUMBER OF PHASES AND PHOTOLUMINESCENSES BETWEEN THE TITANATES PRODUCED BY BOTH TECHNIQUES. IN THE MAH METHOD, THE CONCENTRATIONS OF THE PHASES BT AND ST INCREASES WITH INCREASED CONCENTRATION OF KOH AND THE BT PHASE WITH 6 MOL/L OF SUCH MINERALISER IS OBTAINED WITH A DEFINED MORPHOLOGY AND HIGHER PURITY THAN THE ST PHASE. THE KOH ASSISTS IN THE CO-PRECIPITATION OF HYDROXIDES DURING SYNTHESIS, AND THIS MINERALIZATION HAS A STRONG INFLUENCE ON THE CATION THAT WILL OCCUPY THE SITE A. IN THE SSR METHOD, THE ST PHASE IS OBTAINED AT 1150°C WHILE BT PHASE IS ONLY FORMED AT 1200°C. CHANGES WERE OBSERVED ON THE ENERGY OF THE BAND GAP AND THE PHOTOLUMINESCENCE EMISSION OF THE SAMPLES FOR EACH METHOD OF SYNTHESIS. THE RESULTS SHOW THAT THE ANATASE AS TITANIUM PRECURSOR, IS EFFECTIVE IN THE PROCESS OF SYNTHESIS OF THE TITANATE USING MAH METHOD. THESE MATERIALS HAVE PROPERTIES THAT INDICATE POSSIBILITIES FOR APPLICATIONS IN OPTICAL DEVICES.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por