TITÂNIO E SUAS LIGAS, ATUALMENTE, SÃO UTILIZADOS COMO IMPLANTES POR POSSUIR EXCELENTE RESISTÊNCIA À CORROSÃO E PROPRIEDADES MECÂNICAS MAIS ADEQUADAS QUE OS IMPLANTES DE AÇO INOXIDÁVEL E DE CO-CR. A LIGA DE TITÂNIO MAIS UTILIZADA PARA APLICAÇÕES BIOMÉDICAS É A LIGA TI- 6AL-4V, POREM ESTUDOS MOSTRARAM QUE O VANÁDIO CAUSA REAÇÕES ALÉRGICAS NOS TECIDOS HUMANOS E O ALUMÍNIO TEM SIDO ASSOCIADO COM DESORDENS NEUROLÓGICAS. ASSIM, PARA CONTORNAR ESTE PROBLEMA, NOVAS LIGAS DE TITÂNIO SEM A PRESENÇA DESSES ELEMENTOS ESTÃO SENDO ESTUDADA. O OBJETIVO DESSE TRABALHO É ANALISAR A INFLUÊNCIA DO SOLUTO SUBSTITUCIONAL MOLIBDÊNIO NA ESTRUTURA CRISTALINA, MICROESTRUTURA, MICRODUREZA E MÓDULO DE ELASTICIDADE DE LIGAS TERNÁRIAS DO SISTEMA TI-20ZR-MO, ONDE O TEOR DE MOLIBDÊNIO FOI VARIADO DE 0, 2,5, 5, 7,5 E 10 % EM PESO. A CARACTERIZAÇÃO QUÍMICA DOS MATERIAIS FOI REALIZADA PELA TÉCNICA DE ESPECTROSCOPIA POR EDS, FRX, MAPEAMENTO QUÍMICO E MEDIDAS DE DENSIDADE. A ANÁLISE ESTRUTURAL FOI EFETUADA POR DIFRAÇÃO DE RAIOS X, COM POSTERIOR REFINAMENTO DO DIFRATOGRAMA COM O MÉTODO DE RIETVELD, ANALISANDO A VARIAÇÃO DOS PARÂMETROS DE REDE E QUANTIDADE DE FASES. A ANÁLISE MICROESTRUTURAL FOI REALIZADA PELA DA TÉCNICA DE MICROSCOPIA ÓTICA E ELETRÔNICA DE VARREDURA. UMA ANÁLISE DAS PROPRIEDADES MECÂNICAS DA LIGA É OBTIDA POR INTERMÉDIO DE MEDIDAS DE MICRODUREZA VICKERS E MÓDULO DE ELASTICIDADE DINÂMICO. OS RESULTADOS DE COMPOSIÇÃO QUÍMICA MOSTRARAM QUE AS AMOSTRAS PRODUZIDAS SÃO DE ÓTIMA QUALIDADE. OS RESULTADOS ESTRUTURAIS E MICROESTRUTURAIS INDICAM QUE A LIGA TI-20ZR POSSUI APENAS A FASE α?; A LIGA TI-20ZR-2,5MO COEXISTE AS FASES α? E α?; AS LIGAS TI-20ZR-XMO (X = 5, 7,5 E 10%P.), POSSUEM AS FASES α? E β. OS VALORES DE DUREZA E O MÓDULO DE ELASTICIDADE DAS LIGAS SÃO ALTERADOS COM O ACRÉSCIMO DO TEOR DE MOLIBDÊNIO. A DUREZA AUMENTA, DEVIDO AO ENDURECIMENTO POR SOLUÇÃO SÓLIDA E O MÓDULO DIMINUI COM ALTOS TEORES DE MOLIBDÊNIO DEVIDO À ESTABILIZAÇÃO DA FASE β. A LIGA TI-20ZR- 10MO MOSTROU MELHOR POTENCIAL PARA SER APLICADO COMO UM BIOMATERIAL.

Palavras-Chave (EN):

Resumo Original (EN):

TITANIUM AND ALLOYS CURRENTLY ARE USED AS IMPLANTS POSSESSING EXCELLENT CORROSION RESISTANCE AND MECHANICAL PROPERTIES MORE SUITED TO STAINLESS STEEL IMPLANTS AND CO-CR. THE TITANIUM ALLOY USED FOR MOST BIOMEDICAL APPLICATIONS IS TI-6AL-4V, HOWEVER STUDIES SHOWED THAT VANADIUM CAUSE ALLERGIC REACTIONS IN HUMAN TISSUES AND ALUMINUM HAS BEEN ASSOCIATED WITH NEUROLOGICAL DISORDERS. SO TO OVERCOME THIS PROBLEM, NEW TITANIUM ALLOYS WITHOUT THE PRESENCE OF THESE ELEMENTS ARE BEING STUDIED. THE OBJECTIVE OF THIS STUDY IS TO ANALYZE THE INFLUENCE OF MOLYBDENUM SUBSTITUTIONAL SOLUTE IN THE STRUCTURE, MICROSTRUCTURE, HARDNESS AND ELASTIC MODULUS OF TERNARY ALLOY TI-20ZR-MO SYSTEM, WHERE THE MOLYBDENUM CONTENT WAS VARIED FROM 0, 2.5, 5, 7.5 TO 10% BY WEIGHT. THE CHEMICAL CHARACTERIZATION OF MATERIALS WAS PERFORMED BY SPECTROSCOPY EDS, XRF, CHEMICAL MAPPING AND DENSITY MEASUREMENTS. THE STRUCTURAL ANALYSIS WAS PERFORMED BY X-RAY DIFFRACTION PATTERN WITH REFINEMENT OF THE RIETVELD METHOD, ANALYZING THE VARIATION OF THE LATTICE PARAMETERS AND NUMBER OF PHASES. MICROSTRUCTURAL ANALYSIS WAS PERFORMED BY THE TECHNIQUE OF OPTICAL MICROSCOPY AND SCANNING ELECTRON. AN ANALYSIS OF THE MECHANICAL PROPERTIES OF THE ALLOY IS OBTAINED BY MEANS OF MICROHARDNESS MEASUREMENTS AND DYNAMIC MODULUS OF ELASTICITY. THE CHEMICAL COMPOSITION RESULTS SHOWED THAT THE SAMPLES PRODUCED ARE OF EXCELLENT QUALITY. THE STRUCTURAL AND MICROSTRUCTURAL RESULTS INDICATE THAT TI-20ZR ALLOY CONTAINS ONLY THE α' PHASE; TI-20ZR-2,5MO ALLOY COEXISTS THE α' AND α" PHASES; THE TI-20ZR-XMO ALLOYS (X = 5, 7.5 AND 10 WT.%) HAVING THE PHASE α"AND β. THE VALUES OF HARDNESS AND ELASTIC MODULUS OF ALLOY ARE CHANGED WITH THE INCREASE OF MOLYBDENUM CONTENT. THE HARDNESS INCREASES DUE TO SOLID SOLUTION HARDENING AND THE MODULUS DECREASES WITH HIGHER LEVELS OF MOLYBDENUM DUE TO THE STABILIZATION OF THE β PHASE. THE TI-20ZR-10MO SHOWED THE BEST POTENTIAL TO BE APPLIED AS A BIOMATERIAL.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por