NO PRESENTE TRABALHO FORAM FABRICADOS E CARACTERIZADOS DIFERENTES FILMES DE LANGMUIR E LANGMUIR-BLODGETT (LB) DAS PORFIRINAS DO TIPO TPYP NA FORMA DE BASE LIVRE E DAS PORFIRINAS METALADAS COM COBRE E ZINCO. OS FILMES DE LANGMUIR FORAM CARACTERIZADOS POR TÉCNICA DE PRESSÃO DE SUPERFÍCIE, CURVA DE HISTERESE E TESTE DE ESTABILIDADE. A PARTIR DA CARACTERIZAÇÃO DO FILME DE LANGMUIR, FOI POSSÍVEL DETERMINAR A PRESSÃO DE DEPOSIÇÃO DO FILMES LB, CALCULAR A ÁREA QUE UMA MOLÉCULA OCUPA NA MONOCAMADA E CONCLUIR QUE AS MOLÉCULAS DAS PORFIRINAS ESTUDADAS FORMAM AGREGADOS NA INTERFACE AR-ÁGUA. FILMES LB DO TIPO Y FORAM TRANSFERIDOS PARA DIFERENTES SUBSTRATOS E CARACTERIZADOS POR TÉCNICAS ESPECTROSCÓPICAS TAIS COMO, ABSORÇÃO NA REGIÃO DO ULTRA-VIOLETA/VISÍVEL (UV-VIS), ESPECTROSCOPIA DE ABSORÇÃO NA REGIÃO INFRAVERMELHO (FTIR) E ESPALHAMENTO RAMAN. FOI POSSÍVEL CONCLUIR A PARTIR DA CARACTERIZAÇÃO DOS FILMES LB POR FTIR NOS MODOS DE TRANSMISSÃO E REFLEXÃO, QUE AS MOLÉCULAS APRESENTAM ALGUM ORDENAMENTO ESTRUTURAL. ESSES RESULTADOS INDICAM QUE A PORFIRINA ESTÁ INCLINADA AO PLANO. CORROBORAM COM ESSES RESULTADOS A ÁREA POR MOLÉCULA OBTIDA ATRAVÉS DAS ISOTERMAS DE PRESSÃO. A PORFIRINA DE COBRE NÃO FOI TRANSFERIDA COM SUCESSO PARA OS SUBSTRATOS, NO ENTANTO, FOI FEITO UM ESTUDO SISTEMÁTICO DAS PORFIRINAS NA PRESENÇA DE ACIDO ESTEÁRICO, A FIM DE MELHORAR TAXA DE TRANSFERÊNCIA E ESTABILIDADE DAS PORFIRINAS. OS FILMES LB FORAM APLICADOS COMO SENSORES DO GÁS, OBTENDO RESULTADOS INTERESSANTES QUANDO EXPOSTO A VAPOR HCL. OS FILMES NA PRESENÇA DE ACIDO ESTEÁRICO, TEM UMA MENOR SENSIBILIDADE A HCL, QUE PODE SER EXPLICADO PELA GRANDE INTERAÇÃO ENTRE OS NITROGÊNIOS DO ANEL PORFIRINICO E DO ÁCIDO ESTEÁRICO.

Palavras-Chave (EN):

Resumo Original (EN):

PORPHYRINES POSSESS HIGHLY CONJUGATED, DELOCALIZED π ELECTRON SYSTEMS, WHICH RESULT IN INTENSE UV-VISIBLE ABSORPTION SPECTRA. SOME PORPHYRYN COMPOUNDS EXHIBIT CHANGES IN THEIR OPTICAL ABSORPTION SPECTRA WHEN EXPOSED TO GASEOUS MOLECULES. IN THIS WORK, WE REPORT ON THE CHARACTERIZATION OF 5,10,15,20 TETRAPYRIDILPORPHYRINE (TPYP), CU-TPYP AND ZN-TPYP IN THE FORM OF LANGMUIR AND LANGMUIR-BLODGETT (LB) FILMS. LANGMUIR MONOLAYERS OF PORPHYRINES WERE INVESTIGATED USING SURFACE PRESSURE ISOTHERMS (π-A). THE AREA PER MOLECULE IS CA. 60 Å2 FOR TPYP AND 65 Å2 FOR CU-TPYP AND ZN-TPYP. STABILITY FOR THE LANGMUIR FILMS FROM PORPHYRINES WAS ATTAINED IN HYSTERESIS MEASUREMENTS AFTER TWO COMPRESSION-DECOMPRESSION CYCLES, WITH π-A ISOTHERMS CHANGES TO CA. 25 Å2 FOR TPYP OR 30 Å2 FOR CU AND ZN-TPYP IN THE BEING THE PRACTICALLY THE SAME IN SUBSEQUENT RUNS. THE STABILITY WAS CONFIRMED IN EXPERIMENTS WHERE THE SURFACE PRESSURE WAS KEPT AT 20 MNM-1, WITH DECREASES IN AREA PER MOLECULE OF 14%, 6% AND 6% AFTER 120 MIN FOR TPYP, CU OR ZN-TPYP RESPECTIVELY. LB FILMS WERE TRANSFERRED FROM AN AQUEOUS SUBPHASE, PREPARED FROM ULTRA PURE WATER (MILLI-Q), WITH 1, 5, 15 AND 21 LAYERS DEPOSITED ON QUARTZ SUBSTRATE AND WERE CHARACTERIZED BY UV-VIS. SPECTROSCOPY. Y-TYPE LB FILMS WERE SUCCESSFULLY TRANSFERRED ONTO DIFFERENT SUBSTRATES. THE ELECTRONIC ABSORPTION SPECTRA SHOWS THE SORET AND Q BANDS AT 450, 520 NM RESPECTIVELY AND AGGREGATION OF J-TYPE CAN BE OBSERVED IN THE LB FILMS. THE FILMS WERE DEPOSITED ON SILICON WAFERS AND ANALYZED BY FTIR USING TRANSMISSION AND REFLECTION MODES. THE MAIN BANDS AT 1148 AND 1080 REFERS TO PYROL AND CH BANDS, RESPECTIVELY. SOME ORDERING STRUCTURAL CAN BE NOTED IN LB FILMS AND THE RESULTS POINT TO THE MOLECULE CAN BE INCLINED TO THE PLANE.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por