FILMES FINOS AMORFOS DE CARBONO HIDROGENADO FLUORADOS PRODUZIDOS POR PLASMA POSSUEM PROPRIEDADES EXCELENTES, TAIS COMO BAIXO COEFICIENTE DE ATRITO, BAIXA REATIVIDADE QUÍMICA, ALTA RESISTÊNCIA A ÁCIDOS, ALTA HIDROFOBICIDADE, ALÉM DE PROPRIEDADES ÓPTICAS NOTÁVEIS. NESTE ESTUDO FILMES FINOS FORAM PRODUZIDOS EMPREGANDO PLASMAS DE DESCARGAS LUMINESCENTES CONTENDO DIFERENTES PROPORÇÕES DE GASES EM UMA MISTURA DE C2H2, AR E SF6. O PRESENTE PROJETO VISA A ANÁLISE DAS ALTERAÇÕES DAS PROPRIEDADES ÓPTICAS DOS FILMES PRODUZIDOS A PARTIR DE DIFERENTES CONCENTRAÇÕES DE SF6 NA MISTURA. INVESTIGARAM-SE AS CARACTERÍSTICAS QUÍMICAS DOS FILMES, ATRAVÉS DE ESPECTROSCOPIA DE ABSORÇÃO NO INFRAVERMELHO E ESPECTROSCOPIA DE FOTOELÉTRONS DE RAIOS-X, CONFIRMANDO QUE O AUMENTO DA CONCENTRAÇÃO DE FLÚOR É DEPENDENTE DO AUMENTO DA CONCENTRAÇÃO DE SF6 NA MISTURA DE GASES. AS MEDIDAS DO ÂNGULO DE CONTATO DEMONSTRARAM QUE O AUMENTO DA FLUORAÇÃO DO FILME, AUMENTA SUA HIDROFOBICIDADE. VERIFICOU-SE QUE O ÍNDICE DE REFRAÇÃO DIMINUIU COM O AUMENTO DA FLUORAÇÃO DO FILME. O GAP ÓPTICO FOI CALCULADO POR DUAS TÉCNICAS DIFERENTES, DEMONSTRANDO QUE O AUMENTO DA CONCENTRAÇÃO DE FLÚOR NO FILME TEM RELAÇÃO DIRETA COM O AUMENTO DO GAP ÓPTICO. MODELOS COMPUTACIONAIS PERMITIRAM COMPARAR O GAP ÓPTICO EXPERIMENTAL COM O SEU EQUIVALENTE TEÓRICO, VERIFICANDO QUE O AUMENTO DA DENSIDADE DE LIGAÇÕES C-F AUMENTA O GAP. TAMBÉM FORAM UTILIZADOS MODELOS COMPUTACIONAIS PARA COMPARAR O GAP ÓPTICO TEÓRICO DE FILMES A-C:H:CL E A-C:SI:O:H:F COM OS OBTIDOS EXPERIMENTALMENTE POR TURRI E GONÇALVES EM SEUS TRABALHOS. AS TENDÊNCIAS DO GAP ÓPTICO EM FUNÇÃO DO GRAU DE HALOGENAÇÃO OBTIDAS EXPERIMENTALMENTE E POR MODELAGEM SÃO CONSISTENTES.

Palavras-Chave (EN):

Resumo Original (EN):

AMORPHOUS HYDROGENATED FLUORINATED CARBON THIN FILMS DEPOSITED IN COLD PLASMAS HAVE EXCELLENT PROPERTIES, SUCH AS LOW FRICTION COEFFICIENT, LOW CHEMICAL REACTIVITY, AND HIGH ACID RESISTANCE, AS WELL AS NOTABLE OPTICAL PROPERTIES. IN THIS STUDY, THIN FILMS WERE PRODUCED USING GLOW DISCHARGE PLASMAS FED DIFFERENT PROPORTIONS OF C2H2, AR AND SF6. THE PRESENT PROJECT AIMS TO ANALYZE THE CHANGES IN SOME OPTICAL PROPERTIES OF FILMS PRODUCED AT DIFFERENT PROPORTIONS OF SF6 IN THE MIXTURE. THE CHEMICAL PROPERTIES OF THE FILMS, STUDIED USING INFRARED REFLECTION ABSORPTION SPECTROSCOPY (IRRAS) AND X-RAY PHOTOELECTRON SPECTROSCOPY (XPS), CONFIRM THAT THE FILMS BECOME INCREASINGLY FLUORINATED AT GREATER SF6 FLOW RATES. CONTACT ANGLE MEASUREMENTS SHOWED THAT INCREASES IN THE FILM FLUORINATION, INCREASE ITS HYDROPHOBICITY. THE REFRACTIVE INDEX DECREASES WITH INCREASING FLUORINATION OF THE FILM. THE OPTICAL GAP WAS CALCULATED BY TWO DIFFERENT TECHNIQUES, DEMONSTRATING THAT THE INCREASE IN FLUORINE CONCENTRATION IN THE FILM IS DIRECTLY RELATED TO THE INCREASE IN THE OPTICAL GAP. COMPUTATIONAL MODELS ALLOW COMPARISON OF THE EXPERIMENTAL OPTICAL GAP WITH ITS THEORETICAL EQUIVALENT, VERIFYING THAT AN INCREASE IN THE DENSITY OF C-F BONDS INCREASES THE OPTICAL GAP. COMPUTATIONAL MODELS WERE ALSO USED TO COMPARE THE THEORETICAL OPTICAL GAP OF A-C:H:CL AND A-C:SI:O:H:F FILMS WITH VALUES OBTAINED EXPERIMENTALLY BY TURRI AND GONÇALVES, RESPECTIVELY. THE EXPERIMENTALLY OBSERVED AND MODELED TENDENCIES IN THE OPTICAL GAP AS A FUNCTION OF THE DEGREE OF FILM HALOGENATION ARE CONSISTENT.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por