ESTE TRABALHO TEVE COMO OBJETIVO A INVETIGAÇÃO DA INTERAÇÃO DE RADIAÇÃO GAMA COM TRÊS POLÍMEROS: O POLÍMERO POLI(2-METÓXI, 5-(2'-ETIL-HEXILÓXI)-1,4-FENILENO VINILENO) (MEH-PPV) E OS POLÍMEROS SOLÚVEIS EM ÁGUA POLY {[ 2,5-BIS (2-(N,N-DIETHYLAMINO) ETHOXY) -1,4 -PHENYLENE]-ALT-1,4-PHENYLENE} E O POLY[(2,5-BIS ( 2 ? ( N , N ? DIETHYLAMMONIUM BROMIDE) ETHOXY) ? 1,4 ? PHENYLENE) ? ALT ? 1,4-PHENYLENE]. O POLÍMERO MEH-PPV FOI DISSOLVIDO NOS SOLVENTES ORGÂNICOS CLOROFÓRMIO E BROMOFÓRMIO, JÁ OS OUTROS DOIS POLÍMEROS, EM ÁGUA DESTILADA E SOLUÇÃO DE HCL 1M. AS AMOSTRAS FORAM PREPARADAS EM VÁRIAS CONCENTRAÇÕES E IRRADIADAS COM DOSES QUE VARIARAM DESDE 0,01 GY ATÉ 90 GY, SENDO QUE CADA AMOSTRA FOI IRRADIADA COM APENAS UMA DOSE. OS RESULTADOS FORAM AVALIADOS COM TÉCNICAS ESPECTROSCÓPICAS, SENDO ELAS, ESPECTROSCOPIA DE ABSORÇÃO ÓPTICA UV-VISÍVEL E ESPECTROSCOPIA DE FLUORESCÊNCIA. FOI AVALIADA A ALTERAÇÃO NA POSIÇÃO DO PICO PRINCIPAL DE ABSORÇÃO ÓPTICA COM A DOSE ABSORVIDA PELAS AMOSTRAS. COMO RESULTADO PRINCIPAL, OBSERVOU-SE QUE OS POLÍMEROS SOLÚVEIS EM ÁGUA NÃO APRESENTARAM ALTERAÇÃO ESPECTRAL APÓS SEREM IRRADIADOS. NÃO SENDO INTERESSANTE PARA APLICAÇÃO DOSIMÉTRICA. JÁ PARA AS AMOSTRAS DO POLÍMERO MEH-PPV DILUÍDAS EM BROMOFÓRMIO APRESENTARAM ALTA SENSIBILIDADE PARA DOSES INFERIORES A 1 GY, E APRESENTARAM CERTA LINEARIDADE COM A DOSE RECEBIDA (FATOR IMPORTANTE PARA APLICAÇÃO DOSIMÉTRICA). PARA AS AMOSTRAS EM CLOROFÓRMIO, NÃO FOI OBSERVADO DESLOCAMENTO SIGNIFICATIVO DO ESPECTRO DE ABSORÇÃO PARA DOSES INFERIORES A 1 GY. NO ENTANTO PARA DOSES DE 1 GY À 90 GY, O COMPORTAMENTO OBSERVADO PODE SER DESCRITO POR DUAS REGIÕES LINEARES: UMA COM MAIOR INCLINAÇÃO DA RETA PARA DOSES ATÉ CERCA 30 GY, E OUTRO COM INCLINAÇÃO DA RETA MENOR PARA DOSES ENTRE 30 GY E 90 GY. O COMPORTAMENTO LINEAR, ASSIM COMO A INCLINAÇÃO DA RETA, DO DESLOCAMENTO DA POSIÇÃO DO PICO PRINCIPAL É UM FATOR IMPORTANTE PARA APLICAÇÃO DOSIMÉTRICA. AO MESMO TEMPO, FOI REALIZADO UM ESTUDO DE ESTABILIDADE DAS AMOSTRAS. OBSERVOU-SE QUE AS 11 AMOSTRAS DE MEH-PPV EM BROMOFÓRMIO SOFRERAM GRANDE DEGRADAÇÃO COM 31 DAIS DE ESTOCAGEM, MESMO PARA AS AMOSTRAS NÃO IRRADIADAS. COM ISSO, PROCUROU-SE ACRESCENTAR ALGUM COMPOSTO NA SOLUÇÃO DE BROMOFÓRMIO A FIM DE SE OBTER UMA MELHORA DA ESTABILIDADE, SEM OCASIONAR UMA DIMINUIÇÃO SIGNIFICATIVA NA SENSIBILIDADE DO DOSÍMETRO. PREPAROU-SE AMOSTRAS COM MISTURAS ENTRE BROMOFÓRMIO E CLOROFÓRMIO COM VARIAS PROPORÇÕES ENTRE OS SOLVENTES. UMA DELAS APRESENTOU O DESLOCAMENTO DO ESPECTRO MUITO INFERIOR AO BROMOFÓRMIO PURO APÓS IRRADIA E OUTRAS DUAS APRESENTARAM DESLOCAMENTO DO PICO PRINCIPAL PRÓXIMO AO BROMOFÓRMIO PURO DEPOIS DE IRRADIADAS, NO ENTANTO, TODAS APRESENTARAM DEGRADAÇÃO COM O TEMPO DE ESTOCAGEM DE 30 DIA. A DEGRADAÇÃO MÁXIMA OBSERVADA FOI DE ATÉ 73 % DA APRESENTADA PELAS AMOSTRAS EM BROMOFÓRMIO. AS ULTIMAS TENTATIVAS FORAM MISTURAS ENTRE BROMOFÓRMIO E TOLUENO. O DESLOCAMENTO ESPECTRAL FOI SUPERIOR AO DAS MISTURAS ENTRE BROMOFÓRMIO E CLOROFÓRMIO, E UM POUCO INFERIOR AO BROMOFÓRMIO. COM A ESTOCAGEM DE 30 DIAS, OBSERVOU-SE UMA DEGRADAÇÃO PEQUENA QUANDO COMPARADO COM AS OUTRAS AMOSTRAS CONTENDO BROMOFÓRMIO. A DEGRADAÇÃO MÁXIMA OBSERVADA FOI DE ATÉ 26 % DA APRESENTADA PELAS AMOSTRAS EM BROMOFÓRMIO. POR FIM CONCLUIU-SE QUE O POLÍMERO MEH-PPV EM BROMOFÓRMIO TEM GRANDE POTENCIAL DOSIMÉTRICO PARA DOSES INFERIORES A 1 GY. JÁ NO SOLVENTE CLOROFÓRMIO, ELE APRESENTA UM GRANDE POTENCIAL DOSIMÉTRICO PARA DOSES SUPERIORES A 1 GY. CONCLUIU-SE TAMBÉM QUE APESAR DE UM GRANDE POTENCIAL DOSIMÉTRICO, AS AMOSTRAS DE MEH-PPV EM BROMOFÓRMIO, APRESENTAM GRANDE DEGRADAÇÃO MESMO SEM SEREM IRRADIADAS. MAIS ESTUDOS SERÃO NECESSÁRIOS PARA ENCONTRAR UM MEIO DE CONTER ESSA DEGRADAÇÃO COM A ESTOCAGEM.

Palavras-Chave (EN):

Resumo Original (EN):

THE SUBJECT OF THIS WORK IS THE INVESTIGATION OF GAMMA RADIATION INTERACTION WITH TREE POLYMERS: THE POLYMER POLY - [2-METHOXY, 5-(2?-ETHYL-HEXYLOXY) PHENYLENE VINYLENE] (MEH-PPV) AND THE WATER-SOLUBLE POLYMERS POLY {[ 2,5-BIS (2-(N,N-DIETHYLAMINO) ETHOXY) -1,4 -PHENYLENE]-ALT-1,4-PHENYLENE} AND POLY[(2,5-BIS ( 2 ? ( N , N ? DIETHYLAMMONIUM BROMIDE) ETHOXY) ? 1,4 ? PHENYLENE) ? ALT ? 1,4-PHENYLENE]. THE MEH-PPV POLYMER WAS DISSOLVED IN ORGANIC SOLVENTS, CHLOROFORM AND BROMOFORM, THE OTHER TWO POLYMERS IN DISTILLED WATER AND 1 M AQUEOUS HCL SOLUTION. THE SAMPLES WERE PREPARED AT VARIOUS CONCENTRATIONS AND IRRADIATED WITH DOSES RANGING FROM 0.01 GY TO 90 GY. THE RESULTS WERE EVALUATED BY SPECTROSCOPIC TECHNIQUES, WHICH WERE, UV-VISIBLE ABSORPTION SPECTROSCOPY AND FLUORESCENCE SPECTROSCOPY. THEY WERE EVALUATED THE CHANGES IN THE POSITION OF MAIN OPTICAL ABSORPTION PEAK WITH THE DOSE ABSORBED BY THE SAMPLES. AS MAIN RESULT, IT WAS OBSERVED THAT WATER-SOLUBLE POLYMERS DID NOT SHOW SPECTRAL CHANGE AFTER BEING IRRADIATED. FOR DOSIMETRIC APPLICATION THIS RESULTS ARE NOT INTERESTING. FOR THE MEH-PPV POLYMER SAMPLES DILUTED IN BROMOFORM PRESENTED HIGHLY SENSITIVE TO DOSES BELOW 1 GY, AND SHOWED SOME LINEARITY WITH THE DOSE RECEIVED. FOR SAMPLES IN CHLOROFORM, DOSES BELOW 1 GY DID NOT SHOWED SIGNIFICANT SHIFT IN THE ABSORPTION SPECTRA. HOWEVER, THE SAMPLES IRRADIATED WITH DOSES FROM 1 GY TO 90 GY, THE BEHAVIOR CAN BE DESCRIBED BY TWO LINEAR REGIONS: ONE WITH A HIGHER SLOPE FOR DOSES UP TO ABOUT 30 GY, AND ANOTHER WITH A LOWER SLOPE FOR DOSES BETWEEN 30 GY AND 90 GY. . A GREATER SLOPE TO DOSES UP TO ABOUT 30 GY, AND ANOTHER WITH LOWER SLOPE TO DOSES BETWEEN 30 AND 90 GY. THE LINEAR BEHAVIOR AND THE SLOPE OF THE MAIN PEAK POSITION IS A IMPORTANT FACTOR FOR DOSIMETRIC APPLICATION. AT THE SAME TIME, A STUDY OF STABILITY OF THE SAMPLES WAS PERFORMED. IT WAS OBSERVED THAT THE MEH-PPV SAMPLES IN BROMOFORM SUFFERED SEVERE DEGRADATION WITH 31 DAYS OF STORAGE, EVEN FOR NON-IRRADIATED SAMPLES. THUS, SOME SUBSTANCES WAS ADDED IN BROMOFORM SOLUTION IN ORDER TO OBTAIN AN IMPROVEMENT IN STABILITY WITHOUT 13 CAUSING A SIGNIFICANT DECREASE IN THE DOSIMETER SENSITIVITY. SAMPLES OF BROMOFORM MIXED WITH CHLOROFORM WERE PREPARED WITH VARIOUS PROPORTIONS BETWEEN THE SOLVENTS. ONE SHOWED A SHIFT OF THE SPECTRUM MUCH LESS THAN THE PURE BROMOFORM AND TWO OTHER SHOWED MAIN PEAK DISPLACEMENTS CLOSE TO PURE BROMOFORM, HOWEVER, ALL SAMPLES SHOWED DEGRADATION WITH STORAGE TIME OF 30 DAYS. THE MAXIMUM OBSERVED DEGRADATION WAS UP TO 73% OF PRESENTED BY THE BROMOFORM SAMPLES. THE LATEST ATTEMPTS WERE MIXED BROMOFORM AND TOLUENE. THE SPECTRAL SHIFT WAS HIGHER THAN THAT FOR BROMOFORM MIXED WITH CHLOROFORM AND SLIGHTLY LOWER THAN BROMOFORM. WITH 30 DAYS OF STORAGE, IT WAS OBSERVED A SMALL DEGRADATION WHEN COMPARED WITH OTHER SAMPLES CONTAINING BROMOFORM. THE MAXIMUM OBSERVED DEGRADATION WAS UP TO 26% OF PRESENTED BY THE BROMOFORM SAMPLES. FINALLY IT WAS CONCLUDED THAT THE MEH-PPV POLYMER IN BROMOFORM HAS GREAT DOSIMETRIC POTENTIAL FOR DOSES BELOW 1 GY. IN THE CHLOROFORM, IT HAS GREAT DOSIMETRIC POTENTIAL FOR DOSES ABOVE 1 GY. IT WAS ALSO CONCLUDED THAT ALTHOUGH A LARGE DOSIMETRIC POTENTIAL, MEH-PPV SAMPLES IN BROMOFORM SOLUTION SHOW HIGH DEGRADATION EVEN WITHOUT BEING IRRADIATED. MORE STUDIES ARE NEEDED TO FIND A WAY TO PREVENT THIS DEGRADATION.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por