O OBJETIVO DESTE TRABALHO FOI SINTETIZAR NANOPARTÍCULAS MONOFÁSICAS PARAMAGNÉTICAS DE FERRITA DE NÍQUEL E ZINCO, NI0,5ZN0,5FE2O4 (NZF) E UTILIZÁ-LAS NA PREPARAÇÃO DE FILMES ELASTOMÉRICOS FUNCIONAIS. NANOPARTÍCULAS FORAM SINTETIZADAS POR ROTA QUÍMICA, MÉTODO POLIOL MODIFICADO E CALCINADAS EM DIFERENTES TEMPERATURAS DE FORMA A MODIFICAR SEU TAMANHO. A CARACTERIZAÇÃO ESTRUTURAL DAS NANOPARTÍCULAS FOI REALIZADA VIA ESPECTROSCOPIA VIBRACIONAL DE ABSORÇÃO NA REGIÃO DO INFRAVERMELHO (FTIR), ONDE FOI POSSÍVEL INVESTIGAR AS VIBRAÇÕES CARACTERÍSTICAS DA FASE TIPO ESPINÉLIO ENTRE 500 A 600 CM-1 E 400 CM-1, DIFRATOMETRIA DE RAIOS X (DRX), MICROSCOPIA ELETRÔNICA DE TRANSMISSÃO (MET), NO QUAL FOI POSSÍVEL IDENTIFICAR A FORMAÇÃO DE NANOPARTÍCULAS MONOFÁSICAS DE NI0,5ZN0,5FE2O4 DE ACORDO COM FICHA JCPDS-08-0234, COM TAMANHO ENTRE 14 A 20 NM. A CARACTERIZAÇÃO TÉRMICA DOS PRECURSORES DAS NANOPARTÍCULAS FOI REALIZADA UTILIZANDO AS TÉCNICAS DE CALORIMETRIA EXPLORATÓRIA DIFERENCIAL (DSC) E TERMOGRAVIMETRIA (TG). NANOCOMPÓSITOS COM MATRIZ DE BORRACHA NATURAL VULCANIZADA FORAM PREPARADOS UTILIZANDO DIFERENTES CONCENTRAÇÕES E TAMANHOS DE NANOPARTÍCULAS PARAMAGNÉTICAS, AS QUAIS FORAM ADICIONADAS AOS DEMAIS COMPONENTES NECESSÁRIOS À VULCANIZAÇÃO DA BORRACHA NATURAL (BN) DO TIPO CREPE CLARO BRASILEIRO. A ANÁLISE ESTRUTURAL DOS NANOCOMPÓSITOS, DENOMINADOS DE BN/NZF, FOI REALIZADA UTILIZANDO AS TÉCNICAS DE DIFRATOMETRIA DE RAIOS X (DRX), ESPECTROSCOPIA VIBRACIONAL DE ABSORÇÃO NA REGIÃO DO INFRAVERMELHO (FTIR), MICROSCOPIA ÓPTICA (MO), MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) E MICROSCOPIA DE FORÇA ATÔMICA (AFM). ATRAVÉS DESTAS TÉCNICAS, A INCORPORAÇÃO DE DIFERENTES PROPORÇÕES E TAMANHOS DE NANOPARTÍCULAS FOI AVALIADA. A CARACTERIZAÇÃO TÉRMICA DOS NANOCOMPÓSITOS FOI REALIZADA UTILIZANDO AS TÉCNICAS DE CALORIMETRIA EXPLORATÓRIA DIFERENCIAL (DSC), TERMOGRAVIMETRIA (TG), ANÁLISE DINÂMICO-MECÂNICA (DMA) COM INTUITO DE OBSERVAR AS MODIFICAÇÕES NO COMPORTAMENTO DA BORRACHA NATURAL COM A ADIÇÃO DAS NANOPARTÍCULAS PARAMAGNÉTICAS. O COMPORTAMENTO MAGNÉTICO DAS NANOPARTÍCULAS E NANOCOMPÓSITOS FOI INVESTIGADO POR MAGNETOMETRIA DE AMOSTRA VIBRANTE (VSM) À TEMPERATURA AMBIENTE, NO QUAL FOI POSSÍVEL IDENTIFICAR UM CARÁTER SUPERPARAMAGNÉTICO E FERRIMAGNÉTICO NOS NANOCOMPÓSITOS. A CARACTERIZAÇÃO ELÉTRICA E DIELÉTRICA DAS NANOPARTÍCULAS E NANOCOMPÓSITOS FOI INVESTIGADA ATRAVÉS DA TÉCNICA DE ESPECTROSCOPIA DE IMPEDÂNCIA.

Palavras-Chave (EN):

Resumo Original (EN):

THIS PROJECT AIMS TO THE SYNTHESIS OF SINGLE-PHASE PARAMAGNETIC NANOPARTICLES OF NI0,5ZN0,5FE2O4 (NZF) NICKEL ZINC FERRITE AND ITS APPLICATION IN THE DEVELOPMENT OF FUNCTIONAL NANOCOMPOSITES, IN SPECIFIC MATERIALS WITH POTENTIAL FOR MICROWAVE ABSORBER. MODIFIED POLYOL METHOD WAS USED TO SYNTHESIZE A PRECURSOR POWDER, WHICH WAS CALCINED AT DIFFERENT TEMPERATURES IN ORDER TO ATTAIN NANOPARTICLES WITH DIFFERENT SIZE PARTICLES. STRUCTURAL CHARACTERIZATION OF NANOPARTICLES WAS CARRIED OUT BY ABSORPTION SPECTROSCOPY IN THE INFRARED REGION WITH FOURIER TRANSFORMED (FTIR), X-RAY DIFFRACTION (XRD) AND TRANSMISSION ELECTRON MICROSCOPY (MET). FROM FTIR TECHNIQUE WAS POSSIBLE TO INVESTIGATE CHEMICAL BONDS AND THE NI0,5ZN0,5FE2O4 PHASE FORMATION. THE EVOLUTION OF THE THERMAL BEHAVIOR OF BOTH PRECURSOR POWDER AND NANOPARTICLES WAS PERFORMED USING THE DIFFERENTIAL SCANNING CALORIMETRY (DSC) AND THERMOGRAVIMETRY (TG). NANOCOMPOSITES OF VULCANIZED NATURAL RUBBER WERE PREPARED USING DIFFERENT CONCENTRATIONS OF NI0,5ZN0,5FE2O4 NANOPARTICLES, WHICH WERE ADDED TO OTHER COMPONENTS NECESSARY TO THE VULCANIZATION PROCESS OF NATURAL RUBBER (NR), HEVEA BRASILIENSIS - CLONE RRIM 600. THE STRUCTURAL ANALYSIS OF NANOCOMPOSITES OF VULCANIZED NATURAL RUBBER CONTAINING AS ADDITIVES DIFFERENT FRACTIONS OF NICKEL ZINC FERRITE CALLED HERE AS NR/NZF WAS CONDUCTED BY USE OF TECHNIQUES: XRD, FTIR, OPTICAL MICROSCOPY (OM), SCANNING ELECTRON MICROSCOPY (SEM) AND ATOMIC FORCE MICROSCOPY (AFM). THERMAL ANALYSES OF NANOCOMPOSITES WERE PERFORMED USING DSC, TG, DYNAMIC MECHANICAL ANALYSIS (DMA) IN ORDER TO IDENTIFY CHANGES IN BEHAVIOR OF VULCANIZED NATURAL RUBBER, AS A FUNCTION OF FRACTION OF NI0,5ZN0,5FE2O4 NANOPARTICLES. THE MAGNETIC BEHAVIOR OF BOTH NANOPARTICLES AND NANOCOMPOSITES WERE INVESTIGATED BY THE VIBRATING SAMPLE MAGNETOMETER (VSM) TECHNIQUE, AT ROOM TEMPERATURE. THE ELECTRICAL AND DIELECTRIC CHARACTERIZATION OF NANOPARTICLES AND NANOCOMPOSITES WAS INVESTIGATED BY IMPEDANCE SPECTROSCOPY.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por