NESTE TRABALHO SERÁ APRESENTADA A OBTENÇÃO E CARACTERIZAÇÃO DE COMPÓSITOS A PARTIR DE RASPA INDUSTRIAL DE COURO BOVINO COM BORRACHA NATURAL ENFARDADA TIPO CREPE CLARO (CCB-1) COMO MATRIZ POLIMÉRICA E LIGNINA ATUANDO COMO REFORÇANTE NATURAL. OS COMPÓSITOS FORAM PREPARADOS SOB PRESSÃO À ALTA TEMPERATURA COM PROPORÇÕES DE COURO VARIANDO DE ENTRE 20 PHR E 80 PHR E OS DEMAIS CONSTITUINTES COM QUANTIDADES FIXAS. OS ESTUDOS DE CARACTERIZAÇÃO FORAM REALIZADOS ATRAVÉS DAS TÉCNICAS DE ANÁLISES TÉRMICAS (DSC, TG E DMA), ESPECTROSCOPIA POR INFRAVERMELHO FT-IR MODO ATR E TG/FT-IR ACOPLADOS, ENSAIO MECÂNICO (TENSÃO X DEFORMAÇÃO), IMPERMEABILIDADE A VAPOR, ENSAIO DE RESISTÊNCIA À ABRASÃO E ENSAIO DE RESISTÊNCIA A DOBRA DA SOLA DE COURO (QUEBRA DA FLOR), MICROSCOPIA ÓPTICA (MO). AS PROPRIEDADES FÍSICAS E TERMOMECÂNICAS, TERMOGRAVIMÉTRICAS E MORFOLÓGICAS FORAM ESTUDADAS PARA AVALIAR A COMPATIBILIDADE ENTRE OS CONSTITUINTES DA AMOSTRA PARA QUE POSSA HAVER REPRODUTIBILIDADE DO COMPÓSITO EM LARGA ESCALA SEM PERDER PROPRIEDADES MECÂNICAS FUNDAMENTAIS TANTO DA BORRACHA NATURAL COMO DO COURO. A RASPA DE COURO É UM RESÍDUO ABUNDANTE NA INDÚSTRIA DE COURO E INDESEJÁVEL POR POSSUIR CR+3, QUE SE FOR OXIDADO PODE CHEGAR A CR+6, PRODUTO ALTAMENTE TÓXICO PARA OS SERES VIVOS. ESTE PROJETO TEM UM APELO AMBIENTAL COM OBJETIVO DE DAR UM DESTINO AOS RESÍDUOS INDUSTRIAIS DE COURO, SENDO DESENVOLVIDO UM PRODUTO COM ALTA FLEXIBILIDADE E BOAS PROPRIEDADES MECÂNICAS, DENOMINADO COURO ECOLÓGICO, VISANDO APLICAÇÕES INDUSTRIAIS. EM NOSSO GRUPO DE PESQUISA JÁ FORAM DESENVOLVIDOS DOIS TRABALHOS UTILIZANDO ESTE RESÍDUO DE COURO, PORÉM, OS MATERIAIS DESENVOLVIDOS DIFEREM-SE DO VI COURO ECOLÓGICO EM ALGUMAS PROPRIEDADES. O PRIMEIRO MATERIAL DESENVOLVIDO FOI O COMPÓSITO QUE POSSUI CONDUTIVIDADE ELÉTRICA, OBTIDO A PARTIR DE BORRACHA NATURAL COM RESÍDUO DE COURO E NEGRO DE FUMO, PODENDO SER UTILIZADOS EM PISOS ANTIESTÁTICOS E EM OUTRAS APLICAÇÕES. O SEGUNDO FOI O COMPÓSITO QUE APRESENTA ALTA RIGIDEZ E BAIXA FLEXIBILIDADE, UTILIZANDO BORRACHA NATURAL E RESÍDUO DE COURO, PODENDO SER UTILIZADO EM REVESTIMENTOS E EM CALÇADOS OU EM APLICAÇÕES QUE REQUEREM MATERIAIS RÍGIDOS.

Palavras-Chave (EN):

Resumo Original (EN):

IN THIS WORK IT WILL BE PRESENTED THE PREPARATION AND CHARACTERIZATION OF COMPOSITES FROM INDUSTRIAL LEATHER SCRAPES WITH NATURAL RUBBER CREPE, BALED CLEAR TYPE, AND LIGNIN. THE COMPOSITES WERE PREPARED UNDER HIGH PRESSURE AND TEMPERATURE. THE CHARACTERIZATION STUDIES WERE PERFORMED THROUGH THE THERMAL ANALYSIS TECHNIQUES (DSC, TG AND DMA), FT-IR ABSORPTION SPECTROSCOPY (ATR METHOD) AND COUPLING TG/FT-IR, OPTICAL MICROSCOPY (OM), SCANNING ELECTRON MICROSCOPY (SEM) AND ATOMIC FORCE MICROSCOPY (AFM). THE MECHANICAL PROPERTIES WERE ALSO ANALYZED USING MECHANICAL TESTING (STRESS X STRAIN), IMPERVIOUS TO STEAM, TEST FOR ABRASION RESISTANCE AND BREAKING TEST FLOWER LEATHER SOLE. THE PHYSICAL PROPERTIES, THERMOMECHANICAL, THERMOGRAVIMETRIC AND MORPHOLOGICAL CHARACTERISTICS WERE STUDIED TO ASSESS THE COMPATIBILITY BETWEEN THE SAMPLE CONSTITUENTS IN ORDER TO OBTAIN COMPOSITES WITH LARGE-SCALE REPRODUCIBILITY WITHOUT LOSE FUNDAMENTAL MECHANICAL PROPERTIES OF RUBBER AND LEATHER AS WELL. THE LEATHER SCRAPE IS AN ABUNDANT RESIDUE IN THE LEATHER INDUSTRY AND HAS UNDESIRABLE CR+3, WHICH CAN BE OXIDIZED TO CR+6, PRODUCT HIGHLY DANGEROUS TO LIVING BEINGS. THIS PROJECT HAS AN ENVIRONMENTAL APPEAL WITH THE OBJECTIVE TO DISPOSE THE INDUSTRIAL WASTE LEATHER AND DEVELOP A PRODUCT WITH HIGH FLEXIBILITY AND GOOD MECHANICAL PROPERTIES, KNOWN AS ECOLOGICAL LEATHER, LOOKING FOR INDUSTRIAL APPLICATIONS. IN OUR GROUP OF RESEARCH ALREADY TWO WORKS HAD BEEN DEVELOPED USING THIS LEATHER RESIDUE, HOWEVER, THE DEVELOPED MATERIALS ARE DIFFERED FROM THE ECOLOGICAL LEATHER IN SOME PROPERTIES. THE FIRST MATERIAL DEVELOPED WAS THE COMPOSITES WITH ELECTRICAL PROPERTIES, GOTTEN FROM NATURAL RUBBER WITH LEATHER RESIDUE AND CARBON BLACK, BEING ABLE TO BE USED IN ANTISTATIC FLOOR AND OTHER APPLICATIONS. THE VIII SECOND WAS THE COMPOSITES THAT PRESENT HIGH RIGIDITY AND LOW FLEXIBILITY, USING NATURAL RUBBER AND RESIDUE OF LEATHER, BEING ABLE TO BE USED IN COVERINGS AND SHOES OR IN APPLICATIONS THAT REQUIRE RIGID MATERIALS.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por