ATUALMENTE, EXISTE A NECESSIDADE DE SE ENCONTRAR MATERIAIS CONFIÁVEIS PARA O USO COMO BIOMATERIAIS, PRINCIPALMENTE EM RELAÇÃO ÀS SUAS PROPRIEDADES MECÂNICAS. COM ISSO, PROCURASE LIGAS COM EXCELENTE BIOCOMPATIBILIDADE, PASSIVIDADE QUÍMICA EXTREMA E PROPRIEDADES MECÂNICAS PARA UM BOM COMPORTAMENTO DO MATERIAL A LONGO PRAZO. AMPARADO POR EXCELENTES PROPRIEDADES, O TITÂNIO E SUAS LIGAS TÊM SIDO AMPLAMENTE UTILIZADOS POR VÁRIAS DÉCADAS COMO MATERIAIS PARA IMPLANTES E DISPOSITIVOS MÉDICOS EM TODO MUNDO. A LIGA TI-6AL-4V AINDA É A PRINCIPAL LIGA DE TITÂNIO USADA COMO BIOMATERIAL NO BRASIL, MAS DEVIDO À PREOCUPAÇÃO SOBRE A TOXIDADE DO ALUMÍNIO E DO VANÁDIO A LONGO PRAZO, TÊM SIDO DESENVOLVIDAS NOVAS LIGAS SEM A PRESENÇA DESTES ELEMENTOS. DENTRE AS LIGAS BINÁRIAS ESTUDADAS, A LIGA TI-ZR APRESENTA PROPRIEDADES VANTAJOSAS COMO BOA RESISTÊNCIA A TRAÇÃO, BAIXA DENSIDADE, BOA BIOCOMPATIBILIDADE. NESTE TRABALHO AMOSTRAS DE TI-5%P.ZR E TI-10%P.ZR SÃO SUBMETIDAS A TRATAMENTOS TÉRMICOS DE HOMOGENEIZAÇÃO E DUAS DOPAGENS COM OXIGÊNIO PARA VERIFICAR A INFLUENCIA DO PROCESSAMENTO NAS PROPRIEDADES DAS LIGAS. AS AMOSTRAS FORAM CARACTERIZADAS ATRAVÉS DE MEDIDAS DE DENSIDADE, MICRODUREZA, DIFRAÇÃO DE RAIOS X COM ANÁLISE DE RIETVELD, ANÁLISE QUÍMICA, ANÁLISE DE GASES E ENSAIOS DE CITOTOXICIDADE. ENSAIOS NO PÊNDULO DE TORÇÃO REVELAM O ESPECTRO ANELÁSTICO DAS AMOSTRAS E A RESPOSTA ELÁSTICA DO MESMO EM FUNÇÃO DA TEMPERATURA. ATRAVÉS DOS RESULTADOS PODE-SE OBTER UMA RELAÇÃO ENTRE A CONCENTRAÇÃO DE OXIGÊNIO E AS PROPRIEDADES MECÂNICAS, ESTRUTURAIS E BIOCOMPATIBILIDADE DAS LIGAS ESTUDADAS.

Palavras-Chave (EN):

Resumo Original (EN):

NOWADAYS, THERE IS A NEED TO FIND RELIABLE MATERIAL FOR USE AS BIOMATERIALS, ESPECIALLY IN RELATION TO THEIR MECHANICAL PROPERTIES. WITH THIS COMES THE SEARCH FOR ALLOYS WITH EXCELLENT BIOCOMPATIBILITY, EXTREME CHEMICAL PASSIVITY AND MECHANICAL PROPERTIES IN AN EFFORT TO CREATE A SATISFACTORY LONG-TERM MATERIAL. WITH THE SUPPORT OF EXCELLENT PROPERTIES, TITANIUM AND ITS ALLOYS HAVE BEEN WIDELY USED FOR SEVERAL DECADES AS MATERIALS FOR ORTHOPEDIC AND DENTAL IMPLANTS AND MEDICAL DEVICES WORLDWIDE. THE TI-6AL-4V ALLOY IS STILL THE MAIN TITANIUM ALLOY USED AS A BIOMATERIAL IN BRAZIL, BUT DUE TO CONCERNS ABOUT THE LONG-TERM TOXICITY OF ALUMINUM AND VANADIUM, NEW ALLOYS HAVE BEEN DEVELOPED WITHOUT THE PRESENCE OF THESE ELEMENTS. AMONG THE BINARY ALLOYS STUDIED, TI-ZR HAS ADVANTAGEOUS PROPERTIES SUCH AS GOOD TENSILE STRENGTH, LOW DENSITY, GOOD BIOCOMPATIBILITY. IN THIS WORK SAMPLES OF TI-5% P.ZR AND TI-10% P.ZR ARE SUBJECTED TO HEAT TREATMENT AND HOMOGENIZATION OF TWO DOPING WITH OXYGEN TO CHECK THE INFLUENCE OF PROCESSING ON THE PROPERTIES OF ALLOYS. THE SAMPLES WERE CHARACTERIZED BY DENSITY MEASUREMENTS, MICROHARDNESS, X-RAY DIFFRACTION WITH RIETVELD ANALYSIS, CHEMICAL ANALYSIS, ANALYSIS OF GASES AND IN VITRO CYTOTOXICITY TESTS. TORSION PENDULUM TESTS SHOW THE ANELASTIC SPECTRUM OF SAMPLES AND THE SAME ELASTIC RESPONSE AS A FUNCTION OF TEMPERATURE. THROUGH THE RESULTS WE CAN OBTAIN A RELATIONSHIP BETWEEN OXYGEN CONCENTRATION AND MECHANICAL PROPERTIES, STRUCTURAL AND BIOCOMPATIBILITY OF THE ALLOYS STUDIED.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por