O PRESENTE TRABALHO TEVE POR FINALIDADE PREPARAR, PELO MÉTODO SOL-GEL, BIOCIDAS INORGÂNICOS (CATALISADORES) A BASE DE ÓXIDO DE TITÂNIO (OU TITÂNIA, TIO2), MODIFICADOS OU NÃO COM PRATA E/OU ÓXIDO DE SILÍCIO (OU SÍLICA, SIO2), NA FORMA DE PÓ, PARA A DESINFECÇÃO DE ÁGUAS. OS MATERIAIS PREPARADOS FORAM TESTADOS PARA INATIVAÇÃO DAS BACTÉRIAS PADRÕES ATCC, ESCHERICHIA COLI E PSEUDOMONAS AERUGINOSA, EM REATORES UTILIZADOS EM FOTOCATÁLISE HETEROGÊNEA. EM BAIXAS TEMPERATURAS DE CALCINAÇÃO (250°C E 450°C), OS CATALISADORES SÃO MONOFÁSICOS (TITÂNIA NA FASE ANATÁSIO, AN), INDEPENDENTES DAS MODIFICAÇÕES (ADIÇÃO DE PRATA E/OU SÍLICA). POR OUTRO LADO, A CRISTALINIDADE DAS AMOSTRAS DIMINUI ENQUANTO A ÁREA SUPERFICIAL AUMENTA COM O AUMENTO DA QUANTIDADE DOS MODIFICADORES. QUANDO A TEMPERATURA DE TRATAMENTO É DE 900OC, AS AMOSTRAS ESTRUTURAM-SE SOB FORMA DE TITÂNIA RUTILO (RT), SENDO QUE NA PRESENÇA DE PRATA, ELA É SEGREGADA. QUANDO AS AMOSTRAS DE TIO2 SÃO MODIFICADAS POR SÍLICA, A TRANSIÇÃO PARA A FASE RUTILO É DIFICULTADA E A TITÂNIA PERMANECE ESTRUTURADA SOB FORMA DE ANATÁSIO. COM A ADIÇÃO DE PRATA À MISTURA TITÂNIA-SÍLICA, SOMENTE 10% PERMANECE NA FORMA DE ANATÁSIO E 90% SOFRE A TRANSIÇÃO PARA RUTILO. OS RESULTADOS DE FTIR CONFIRMAM QUE A ADIÇÃO DE MODIFICADORES NÃO INTRODUZ MUDANÇAS SIGNIFICATIVAS AOS GRUPOS SUPERFICIAIS. A PRESENÇA DO SILÍCIO E PRATA NO MATERIAL NÃO ALTEROU AS POSIÇÕES DAS BANDAS DE TITÂNIA AN (NÃO HÁ INDÍCIOS DE FORMAÇÃO DE SOLUÇÃO SÓLIDA), SENDO QUE UMA BANDA ADICIONAL ASSOCIADA AO GRUPO SI-O PARA AS AMOSTRAS CONTENDO ESTE MODIFICADOR FOI OBSERVADA. OS TESTES BACTERICIDAS, FEITOS SOB IRRADIAÇÃO (365 NM) E NO ESCURO, MOSTRARAM QUE TIO2 MODIFICADO COM A PRATA ACELERA A INATIVAÇÃO DAS BACTÉRIAS E É ATIVO MESMO NA AUSÊNCIA DE LUZ. NÃO SE OBSERVA UMA INFLUÊNCIA CLARA DA TEMPERATURA DE CALCINAÇÃO (ESTRUTURA CRISTALOGRÁFICA DO SUPORTE E DA FASE ATIVA) NA ATIVIDADE ANTIMICROBIANA, POIS MATERIAIS COM O SUPORTE RUTILO TAMBÉM APRESENTAM UMA BOA ATIVIDADE. TODAVIA, TEMPERATURAS DE TRATAMENTO ENTRE 250 E 900OC SÃO REQUERIDAS PARA OTIMIZAR A ATIVIDADE. A SÍLICA DIMINUI A ATIVIDADE, APESAR DAS PROPRIEDADES TEXTURAIS (ÁREA SUPERFICIAL, POROSIDADE) SEREM AQUELAS QUE FAVORECEM A ATIVIDADE.

Palavras-Chave (EN):

Resumo Original (EN):

THIS STUDY AIMED TO PREPARE INORGANIC BIOCIDES BASED ON TIO2, MODIFIED OR NOT BY SILVER AND/OR SIO2 (POWDER), BY THE SOL-GEL METHOD, TO BE USED FOR TREATMENT OF CONTAMINATED WATER. THE ABILITY TO INACTIVATE BACTERIA (ATCC STANDARD) AS ESCHERICHIA COLI AND PSEUDOMONAS AERUGINOSA WAS TESTED IN A REACTOR USED IN HETEROGENEOUS PHOTOCATALYSIS. THE SAMPLES ARE STRUCTURED AS SINGLE PHASE (ANATASE TITANIA, AN) AT LOW TEMPERATURES OF CALCINATION (250°C AND 450°C) EVEN IN THE PRESENCE OF SILVER AND/OR SILICA. THEIR CRYSTALLINITY DECREASES WITH INCREASING AMOUNT OF MODIFIERS WHILE THE SURFACE AREA INCREASES. THE SAMPLE, WITHOUT MODIFIERS, IS STRUCTURED AS THE RUTILE TITANIA (RT) WHEN TREATED AT 900OC AND, IN THE PRESENCE OF SILVER, THIS METAL SEGREGATES. WHEN THE SAMPLES ARE MODIFIED BY SILICA, THE TRANSITION TO RUTILE IS SUPPRESSED AND TITANIA REMAINS AS ANATASE. ADDING SILVER TO TITANIA-SILICA MIXTURE, 90% OF TITANIA TRANSFORMS TO RUTILE BUT 10% STILL REMAIN AS ANATASE. THE FTIR RESULTS CONFIRM THAT THE ADDITION OF MODIFIERS DOES NOT INTRODUCE SIGNIFICANT CHANGE IN THE SURFACE GROUPS. THE PRESENCE OF SILICON AND SILVER IN THE MATERIAL DOES NOT CHANGE THE POSITIONS OF THE AN TITANIA BANDS, EXHIBITING AN ADDITIONAL BAND ATTRIBUTED TO THE SI-O GROUP. THE BACTERICIDAL TESTS, CARRIED OUT UNDER IRRADIATION (365 NM) AND IN THE DARK, SHOWED THAT TIO2 MODIFIED WITH SILVER ACCELERATES THE INACTIVATION OF BACTERIA AND THAT IT IS ACTIVE EVEN IN THE ABSENCE OF LIGHT. THE INFLUENCE OF THE CALCINATION TEMPERATURE (CRYSTALLOGRAPHIC STRUCTURE OF THE SUPPORT AND ACTIVE PHASE) ON THE BACTERICIDAL ACTIVITY IS NOT CLEAR, SINCE SAMPLES BASED ON RUTILE SUPPORT ALSO EXHIBIT GOOD ACTIVITY. ANYWAY, TEMPERATURES BETWEEN 250 AND 900°C ARE REQUIRED TO OPTIMIZE THE ACTIVITY. THE SILICA DECREASES THE ACTIVITY ALTHOUGH THE TEXTURAL PROPERTIES (SURFACE AREA, POROSITY) ARE THOSE THAT FAVOR THE ACTIVITY.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por