Título Original (PT):

Local de Publicação:

Data de Publicação:

Área de Concentração:

Banca Examinadora:

Palavras-Chave (PT):

Resumo Original (PT):

NESTE TRABALHO DE DISSERTAÇÃO DE MESTRADO FORAM PREPARADAS AMOSTRAS DO SISTEMA PB1-X-YCAXSRYTIO3 (PCST) COM X = 0.05, 0,15, 0,35 E Y = 0,05, 0.15, 0,35, UTILIZANDO-SE O MÉTODO DOS PRECURSORES POLIMÉRICOS E, A PARTIR DESSE MATERIAL, PRODUZIR AMOSTRAS CERÂMICAS E FILMES FINOS NANOESTRUTURADOS E CARACTERIZAR SUAS PROPRIEDADES ESTRUTURAIS, MICROESTRUTURAIS E ELÉTRICAS. A CARACTERIZAÇÃO ESTRUTURAL FOI REALIZADA UTILIZANDO AS TÉCNICAS DE DIFRAÇÃO DE RAIOS X, ESPECTROSCOPIA RAMAN E ESPECTROSCOPIA NA REGIÃO DO INFRAVERMELHO. OS FILMES FINOS FORAM PREPARADOS PELA TÉCNICA ?SPIN-COATING? SOBRE SUBSTRATO DE SI/SIO2/TI/PT. A TEMPERATURA DE CRISTALIZAÇÃO FOI DE 600ºC. A CRISTALIZAÇÃO DE TODOS OS FILMES FINOS E PÓ APRESENTARAM ESTRUTURA DO TIPO PEROVISQUITA SEM A PRESENÇA DE UMA SEGUNDA FASE. FOI POSSÍVEL OBTER COM SUCESSO UM SISTEMA COMPLEXO DE INCORPORAÇÃO DE DOIS DIFERENTES ÍONS (CA2+ E SR2+) NO SITIO A, EM SUBSTITUIÇÃO AOS ÍONS PB2+ PARA O SISTEMA PB1-X-YCAXSRYTIO3 NA FORMA DE FILME FINO E PÓ, SEM A SEPARAÇÃO DE FASES TAIS COMO PBTIO3, CATIO3, SRTIO3, OU ATÉ MESMO FASE COMPLEXAS COMO (PB,SR)TIO3 OU (PB,CA)TIO3. OS SÍTIOS A LOCALIZAM-SE DENTRO DE UM DODECAEDRO (AO12) DE DOZE OXIGÊNIOS ENQUANTO O SITIO B NO INTERIOR DE UM OCTAEDRO REGULAR (BO6) CONSTITUÍDO DE OITO OXIGÊNIOS. PORTANTO, AS DISTORÇÕES OCORRIDAS NESTAS ESTRUTURAS PRODUZEM IMPORTANTES MUDANÇAS E SURGIMENTO DE NOVAS PROPRIEDADES ELÉTRICAS QUE ENCADEIAM GRANDE INTERESSE TECNOLÓGICO E CIENTIFICO. AS PROPRIEDADES FERROELÉTRICAS FORAM FORTEMENTE INFLUENCIADAS PELA PRESENÇA DESSES DOIS ÍONS (CA2+ E SR2+) EM SUBSTITUIÇÃO AOS ÍONS PB2+. LEVANDO O SISTEMA A UMA COMPLETA AUSÊNCIA DE NATUREZA FERROELÉTRICA A TEMPERATURA AMBIENTE.

Palavras-Chave (EN):

Resumo Original (EN):

ON THIS MASTER?S DEGREE DISSERTATION SAMPLES OF THE SYSTEM PB1-X-YCAXSRYTIO3 (PCST) WITH X = 0.05, 0.15, 0.35 AND Y = 0.05, 0.15, 0.35 WERE PREPARED THROUGH THE POLYMERIC PRECURSORS METHOD. FROM THIS MATERIAL, CERAMIC SAMPLES AND THIN FILMS WERE PRODUCED AND THEIR STRUCTURE, MICROSTRUCTURE AND ELECTRICAL PROPERTIES WERE ASSESSED. THE STRUCTURAL CHARACTERIZATION WAS DONE USING X-RAY DIFFRACTION, RAMAN SPECTROSCOPY AND SPECTROSCOPY TECHNIQUES ON THE INFRARED REGION. THE FILMS WERE PREPARED THROUGH THE SPIN-COATING TECHNIQUE ON SI/SIO2/TI/PT SUBSTRATE AND ITS CRYSTALLIZATION TEMPERATURE WAS 600ºC. ALL THIN FILMS AND POWDER SHOWED STRUCTURE LIKE PEROVSKITE WITHOUT A SECOND PHASE. A COMPLEX INCORPORATION SYSTEM OF TWO DIFFERENT IONS (CA2+ AND SR2+) AT SITE A WAS SUCCESSFULLY ACHIEVED, REPLACING THE PB2+ IONS ON THE PB1-X-YCAXSRYTIO3 SYSTEM AS THIN FILM AND POWDER WITH NO PARTITION OF PHASES SUCH AS PBTIO3, CATIO3, SRTIO3, OR EVEN MORE COMPLEX ONES AS (PB,SR)TIO3 OR (PB,CA)TIO3. THE SITES A WERE FOUND IN A (AO12) DODECAHEDRON OF TWELVE OXYGENS, AND THE SITE B WAS DISCOVERED IN A REGULAR OCTAHEDRON FORMED BY EIGHT OXYGENS. THEREFORE THE DISTORTIONS ON THESE STRUCTURES TRIGGERED RELEVANT CHANGES AND NEW ELECTRICAL PROPERTIES WHICH PROMOTE GREAT TECHNOLOGICAL AND SCIENTIFIC INTEREST. IT IS NOTEWORTHY THAT THE FERROELECTRIC PROPERTIES WERE HEAVILY INFLUENCED BY THE PRESENCE OF THESE TWO IONS (CA2+ AND SR2+) REPLACING THE PB2+ IONS, LEADING THE SYSTEM TO AN ABSOLUTE ABSENCE OF FERROELECTRIC NATURE AT ROOM TEMPERATURE.

Tempo Estimado Para Download:

Última Visita em :

Último Download em :

UNESP - Universidade Estadual Paulista "Júlio de Mesquita Filho"

Tecnologia, Desenvolvimento, e Layout:
Assessoria de Informática - Grupo de Tecnologia da Informação

Protegido por